Aluminum Welding Wire, Welding Wire, Er5183 manufacturer / supplier in China, offering Manufacturer/Aluminum Welding Wire Er5183 (MIG/TIG), TIG MIG Copper Welding Wire 1.6mm Em12, 1.6mm CO2 MIG Er70s-6 Welding Wire and so on.

(/ )

Supplier Homepage Product Aluminium Welding Wire Manufacturer/Aluminum Welding Wire Er5183 (MIG/TIG)

Manufacturer/Aluminum Welding Wire Er5183 (MIG/TIG)

Purchase Qty.:
(Tons)
1-4 5+
FOB Unit Price: US $5,400 US $5,350
Purchase Qty. (Tons) FOB Unit Price
1-4 US $5,400
5+ US $5,350
Get Latest Price
Port: Tianjin, China
Production Capacity: 2000 Tons Per Year
Payment Terms: L/C, T/T, D/P

Request a custom order and have something just for you!

Send Customized Request
Basic Info
  • Model NO.: AWS ER5183
  • Material: Aluminum / Aluminum Alloy
  • Size: 1.6mm-4.0mm
  • Raw Material: Aluminum
  • Logo: Luhan
  • Transport Package: as Your Request
  • Origin: China
  • Type: Rolling Wire
  • Flux Containing: Not Containing Flux
  • Weight: 5kg,10kg
  • Spool Material: Plastic
  • Trademark: LUHAN
  • Specification: 1.6mm-4.0mm
  • HS Code: 72292000
Product Description
ER5183
DIN EN ISO 18273
S AL 5183 (AlMg 4, 5 Mn 0, 7)

Werkstoff-Nr.
3.3548
AWS/ASME A 5.10
ER 5183

Performance&Usage
ER5183 is with nearly 5% magnesium and some of manganese. And this product is of high toughness, good forgeability, and well anti-corrosiveness, Furthermore, this is a good choice for color-match in welding after anodic process. But for some alloy, the strength of welding joint is a little higher than 5356.

The model 5183 do not suggested to use in aluminium alloy workpiece which working temperature is over 65º C, thus will cause corrosion cracking in welded joints. You should strictly clean the oxide film on the edge of the workpiece and oil before welding, otherwise it will make bad weld produce and cause porosity, slag inclusion and other defects. Also you can use a plate to hold molten metal to ensure meld form.
The strength of ER5183 is higher than ER5356, which used in high strength situation, especially for crack after welding with other brand or other type aluminium welding wires. SAL5183 is with nearly 5% magnesium and some of manganese. And this product is of high toughness, good forgeability, and well anti-corrosiveness, Furthermore, this is a good choice for color-match in welding after anodic process.
The argon arc welding of Aluminium & Magnesium alloy welding wires is used as the filler material, used in pressure vessel of chemical industry, nuclear industry, ship-building, boiler, space industry, etc.
Chemical component (wt)/%
SiFeCuMnMgCrZnTiBe
OthersOthers total
≤0.05≤0.15
Al
≤0.25≤0.4≤0.10.5~1.04.5~5.20.05~0.25≤0.1≤0.15≤0.0003Rem.
Characteristic
Melting range1075 - 1180°F
Electrical conductivity16~19Ω@m/mm2
Density2.66g/mm3
Anti corrosion performanceA(Gen) A(SCC)
The coefficient of thermal expansion (20  ~300 )23.7×10-6/K
Thermal conductivity (20 )110-120W/m@K
Wire Standard
Classification:
GB10858-2008
ANSI/AWS A5.10-92
Passed ISO9001:2008 Quality Management System
The mechanical properties of the welding joints
MotherboardMotherboard performanceJoint properties
Rm (MPa)RP0.2 (MPa)A/%Rm (MPa)RP0.2 (MPa)A/%
6061-T6/T6513102751220513011
6063-T6240210121358012
7005-T6/T633703151231520510
7039-T644453801331018012
5083-O3102001828512516
6082-T63102751121013010
7039-T614103401432022014
Specifications and packaging

 
Diameter /mmPacking /Kg
MIG0.8\0.9\1.0\1.2\1.6\2.40.5\2\5\6\7
TIG1.6\2.0\2.4\3.0\3.2\4.0\5.0/10005\10
Send your message to this supplier
Avatar
Ms. Nancy
Marketing Manager
*From:
To: Ms. Nancy
*Message:

Enter between 20 to 4,000 characters.

This is not what you are looking for? Post a Sourcing Request Now